Composition and method of forming quantum dot layer with the composition, quantum dot layer and light-emitting device including the quantum dot layer

ABSTRACT

A composition including a block copolymer, a quantum dot precursor, and a solvent, a method of forming a quantum dot layer with the composition, a quantum dot layer formed from the composition, and a light-emitting device including the quantum dot layer.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority under 35 U.S.C. § 119 to Korean Patent Application No. 10-2020-0186769, filed on Dec. 29, 2020, in the Korean Intellectual Property Office, the disclosure of which is herein incorporated by reference in its entirety.

BACKGROUND 1. Field

The present disclosure relates to a composition, a method of forming a quantum dot layer with the composition, a quantum dot layer formed from the composition, and a light-emitting device including the quantum dot layer.

2. Description of the Related Art

There is a demand for light-emitting display apparatuses that have excellent viewing angles, excellent contrast, and quick response speeds, and thus, are drawing much attention as next-generation display apparatuses. Generally, a light-emitting display apparatus has a thin-film transistor and light-emitting devices formed on a substrate. Such light-emitting display apparatuses are utilized as display units in small products such as mobile phones, tablets, and laptops, and are utilized in display units in large products such as televisions or signage.

A light-emitting display apparatus includes a light-emitting device including a pixel electrode, an opposite electrode, and an interlayer including an emission layer between the pixel electrode and the opposite electrode. The interlayer of the light-emitting device may be formed by various methods, for example, a chemical vapor deposition (CVD) method, an inkjet method, and the like.

SUMMARY

Provided are a composition for forming a quantum dot layer having molecular stability, a method of forming a quantum dot layer with the composition, a quantum dot layer formed from the composition, and a light-emitting device including the quantum dot layer.

Additional aspects will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the presented embodiments of the disclosure.

According to an aspect of the disclosure, a composition includes

a block copolymer including an A moiety that is hydrophobic solvent-compatible and a B moiety that is hydrophobic solvent-incompatible,

a quantum dot precursor, and

a hydrophobic solvent, and

wherein the B moiety that is hydrophobic solvent-incompatible includes a —OH moiety, a —(C═O)O— moiety, or any combination thereof.

According to another aspect of the disclosure, a method of forming a quantum dot layer includes coating a substrate with the above composition, removing the solvent from the composition of the coated substrate, and treating the composition from which the solvent has been removed with a weak base.

According to another aspect of the disclosure, a quantum dot layer is formed by the method of forming a quantum dot layer.

According to another aspect of the disclosure, a light-emitting device including the quantum dot layer is described.

Other aspects, features, and advantages other than those described above will become apparent from detailed description, claims and drawings for the following disclosure.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other aspects, features, and advantages of certain embodiments of the disclosure will be more apparent from the following description taken in conjunction with the accompanying drawings, in which:

FIG. 1 is a schematic view of a composition according to an embodiment of the disclosure;

FIG. 2 is a diagram illustrating a process of manufacturing a quantum dot layer using a composition according to an embodiment of the disclosure; and

FIG. 3 is a schematic view of a light-emitting device according to an embodiment of the disclosure.

DETAILED DESCRIPTION

Reference will now be made in detail to embodiments, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout. In this regard, the present embodiments may have different forms and should not be construed as being limited to the descriptions set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Like reference numerals refer to like elements throughout.

The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms, including “at least one,” unless the content clearly indicates otherwise. “At least one” is not to be construed as limiting “a” or “an.” Throughout the disclosure, the expression “at least one of a, b or c” indicates only a, only b, only c, both a and b, both a and c, both b and c, all of a, b, and c, or variations thereof. “Or” means “and/or.” As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. It will be further understood that the terms “comprises” and/or “comprising,” or “includes” and/or “including” when used in this specification, specify the presence of stated features, regions, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, regions, integers, steps, operations, elements, components, and/or groups thereof.

“About” or “approximately” as used herein is inclusive of the stated value and means within an acceptable range of deviation for the particular value as determined by one of ordinary skill in the art, considering the measurement in question and the error associated with measurement of the particular quantity (i.e., the limitations of the measurement system). For example, “about” can mean within one or more standard deviations, or within ±10% of the stated value.

Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the present disclosure, and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

Exemplary embodiments are described herein with reference to cross section illustrations that are schematic illustrations of idealized embodiments. As such, variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are to be expected. Thus, embodiments described herein should not be construed as limited to the particular shapes of regions as illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. For example, a region illustrated or described as flat may, typically, have rough and/or nonlinear features. Moreover, sharp angles that are illustrated may be rounded. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the precise shape of a region and are not intended to limit the scope of the present claims.

A composition according to an aspect of the disclosure may include:

a block copolymer including an A moiety that is hydrophobic solvent-compatible and a B moiety that is hydrophobic solvent-incompatible;

a quantum dot precursor; and

a hydrophobic solvent, and

wherein the B moiety that is hydrophobic solvent-incompatible may include a —OH moiety, a —(C═O)O— moiety, or any combination thereof.

In an embodiment, the solvent may be hydrophobic, and accordingly, at least a portion of the B moieties that are hydrophobic solvent-incompatible, and which includes a —OH moiety, a —(C═O)O— moiety, or any combination thereof, associate in the solvent.

In an embodiment, the block copolymer may include an A moiety that is hydrophobic solvent-compatible and a B moiety that is hydrophobic solvent-incompatible.

In an embodiment, the block copolymer may be present as a spherical micelle in the composition. As would be understood by one of skill in the art, not all of the block copolymer may form or be present in the form of a micelle. However, at least a portion, or even most of the block copolymer may primarily form or be primarily present in the form of a micelle.

In an embodiment, a number average molecular weight of the A moiety may be M₂, a number average molecular weight of the B moiety may be M₁, and M₁ and M₂ may satisfy Equation (1):

M₁/M₂≤⅓  (1).

In a case where a value of M₁/M₂ satisfies Equation (2), the block copolymer may form or may be present as a cylindrical micelle in the composition:

⅓<M₁/M₂≤½  (2).

In a case where a value of M₁/M₂ satisfies Equation (3), the block copolymer may be present as or may form a membrane in the composition:

½<M₁/M₂≤1  (3).

In an embodiment, a number average molecular weight of the block copolymer may be from about 5,000 grams per mole (g/mol) to about 50,000 g/mol. In order to dissolve the block copolymer in a solvent and perform a soluble process, it is appropriate that a number average molecular weight of the block copolymer is within the range described above.

In an embodiment, the block copolymer may be present as a spherical micelle in the composition, and in this case, the B moiety may be directed toward to or form a core of the micelle and the A moiety may be directed toward to or form a shell of the micelle. Again, as would be understood by one of skill in the art, not all of the B or A moieties of all of the block copolymer may form or present in the form of a spherical micelle, or be directed to or form the core or the shell, respectively. However, at least a portion, or even most of the A or B moieties block copolymer may primarily form or be primarily present in the form of a micelle.

The solvent is hydrophobic, and thus, the A moiety that is hydrophobic solvent-compatible forms the shell.

In an embodiment, the block copolymer may be present, i.e., may be primarily present or form a spherical micelle, and the quantum dot precursor may be present, i.e., may be primarily present within the spherical micelle.

In an embodiment, the block copolymer may include poly(styrene)-b-poly(methyl methacrylate) (PS-PMMA), poly(styrene)-b-poly(acrylic acid) (PS-PAA), poly(styrene)-b-poly(ethylene glycol) (PS-PEG), polyethylene glycol-b-polylactic acid (PEG-PLA), poly(ethylene glycol)-b-poly(lactic acid-co-glycolic acid) (PEG-PLGA), poly(ethylene glycol)-b-polycaprolactone (PEG-PCL), polyethylene-block-poly(ethylene glycol) (PE-PEG), or any combination thereof.

In an embodiment, the quantum dot precursor may include a metallic salt. The quantum dot precursor may be a metallic salt formed in combination of a metal cation and an anionic compound. A metal ion of the metallic salt may bind (for example, by a coordinate bond) with the —OH moiety or the —(C═O)O— moiety of the B moiety that is hydrophobic solvent-incompatible.

In an embodiment, the quantum dot precursor may include a nitrate salt of a metal, a chloride salt of a metal, or any combination thereof. In an embodiment, the quantum dot precursor may include silver (Ag), palladium (Pd), iron (Fe), cobalt (Co), niobium (Nb), molybdenum (Mo), tantalum (Ta), tungsten (W), titanium (Ti), nickel (Ni), copper (Cu), cadmium (Cd), zinc (Zn), indium (In), tin (Sn), or any combination thereof, or including a metal nitrate thereof or a metal chloride thereof.

In an embodiment, the quantum dot precursor may include AgNO₃, Pd(NO₃)₂, FeCl₃, COCl₂, NbCl₅, MoCl₅, TaCl₅, WCl₅, TiCl₄, NiCl₂, CuCl₂, CdCl₂, ZnCl₂, InCl₃, SnCl₂, or any combination thereof.

In an embodiment, the solvent may include n-hexane, benzene, toluene, dimethylbenzene, ethylbenzene, or any combination thereof.

FIG. 1 is a schematic view of a composition according to an embodiment of the disclosure. The composition according to an embodiment of the disclosure is described with reference to FIG. 1.

In an embodiment, the composition may include a PS-PMMA block copolymer, ZnCl₂ as the quantum dot precursor, and toluene as the solvent.

When ZnCl₂ is added to a PS-PMMA block copolymer dissolved in toluene, Zn²⁺ binds with methyl methacrylate that is incompatible with toluene in the PS-PMMA block copolymer.

In this case, molecular weights of a polystyrene moiety and a poly(methyl methacrylate) moiety in the PS-PMMA block copolymer may satisfy Equation (1).

The PS-PMMA block copolymer may be present, i.e., primarily present, as a spherical micelle, and ZnCl₂ is present, i.e., primarily present, within the spherical micelle. The PS-PMMA block copolymer may be uniformly dispersed in the composition.

The quantum dot precursor is present, i.e., primarily present, within the spherical micelle, and thus, may be uniformly dispersed in the composition.

In an embodiment, the block copolymer in the composition may be from about 0.1 parts by weight to about 5 parts by weight based on 100 parts by weight of the total composition. When the block copolymer is greater than about 5 parts by weight, a viscosity is observed to be relatively too high, and thus, the composition may be difficult to use in the soluble process of the method described herein. When the block copolymer is less than about 0.1 parts by weight, a viscosity is observed to be relatively too low, and thus, the composition may be difficult to use in the soluble process of the method described herein.

In an embodiment, the quantum dot precursor in the composition may be from about 3 parts by weight to about 10 parts by weight based on 100 parts by weight of the block copolymer. In light of a weight range and a molecular weight range of the block copolymer, the weight range of the quantum dot precursor is within the range described above.

FIG. 2 is a diagram illustrating a process of making a quantum dot layer with a composition according to an embodiment of the disclosure.

A method of forming a quantum dot layer according to another aspect of the disclosure may include:

coating a substrate with the composition described herein;

removing a solvent from the composition of the coated substrate; and

treating the composition from which the solvent has been removed with a weak base.

In an embodiment, the substrate may be a hole injection layer, a hole transport layer, or an emission layer.

In an embodiment, the coating of the substrate with the composition may be performed by a liquid process. In an embodiment, the coating of the substrate with the composition may be performed by a spin coating method, a slit coating method, or an inkjet printing method.

In an embodiment, the removing of the solvent from the composition of the coated substrate may be performed by heating. A heating temperature may be a boiling point temperature of the solvent. In an embodiment, the removing of the solvent from the composition of the coated substrate may be performed by a temperature of about 60° C. to 150° C.

In an embodiment, a pH of the weak base may be greater than about 7 and less than or equal to about 9.

When the composition from which the solvent is removed is treated with a sufficient amount of the weak base for a sufficient period of time, an anion bound to a metal ion is removed and may then be exchanged with another desired anion.

In an embodiment, when NH₄OH_((aq)) is used as a weak base in an amount of 1 mole to 10 moles based on the mole equivalent (eq) of the quantum dot precursor (for example, a metal chloride or metal nitrate) for about 10 seconds to 6 hours, the quantum dot precursor is converted into a metal oxide quantum dot.

In an embodiment, when NH₄OH_((aq)) is used as a weak base in an amount of 1 mole to 10 moles based on the equivalent (eq) of the quantum dot precursor (for example, ZnCl₂) for about 10 seconds to 6 hours, the quantum dot precursor is converted into a quantum dot (ZnO).

A quantum dot layer according to another aspect of the disclosure may be formed by the method of forming a quantum dot layer.

In an embodiment, the quantum dot layer may be an emission layer or an electron transport layer.

A light-emitting device according to another aspect of the disclosure may include the quantum dot layer.

Additional Additives

The composition may further include, as necessary, an adhesion promoter for increasing the adhesion to a substrate, a leveling agent for improving coating properties, an antioxidant, an ultraviolet ray absorbent, or any combination thereof.

The adhesion promoter may be added to improve adhesion to a substrate and may include a silane coupling agent having a reactive substituent selected from a group consisting of a carboxyl group, a (meth)acryloyl group, an isocyanate group, an epoxy group, and a combination thereof, but embodiments of the present disclosure are not limited thereto. In an embodiment, as the silane coupling agent, trimethoxysilylbenzoic acid, γ-methacryloxypropyltrimethoxysilane, vinyltriacetoxysilane, vinyltrimethoxysilane, γ-isocyanatopropyltriethoxysilane, γ-glycidoxypropyltrimethoxysilane, β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, or any combination thereof may be utilized.

The leveling agent is not particularly limited, but a silicon-based compound, a fluorine-based compound, a siloxane-based compound, a nonionic surfactant, an ionic surfactant, a titanate coupling agent, and the like may be utilized as the leveling agent. In an embodiment, the leveling agent may include a silicon-based compound, a fluorine-based compound or a combination thereof.

The silicon-based compound is not particularly limited, but may include dimethyl silicon, methyl silicon, phenyl silicon, methyl phenyl silicon, alkyl modified silicon, alkoxy modified silicon, polyether modified silicon, and the like. In an embodiment, as the silicon-based compound, dimethyl silicon, methyl phenyl silicon, and the like may be utilized.

The fluorine-based compound is not particularly limited, but may include polytetrafluoroethylene, polyvinylidene fluoride, fluoroalkyl (meth)acrylate, perfluoropolyether, perfluoroalkyl ethylene oxide, and the like. In an embodiment, as the fluorine-based compound, polytetrafluoroethylene may be utilized.

The siloxane-based compound is not particularly limited, and may include a dimethyl siloxane compound (Product name: KF96L-1, KF96L-5, KF96L-10, KF96L-100, products of Shin-Etsu Silicone Co., Ltd.).

The above-described leveling agent may be used alone or may be used in combination of two or more types of leveling agent.

An amount of the leveling agent may vary according to a desired performance, but may be from about 0.001 parts by weight to about 5 parts by weight, for example, from about 0.001 parts by weight to about 1 parts by weight, based on the total weight of the composition. When the amount of the leveling agent is within the above-described range, fluidity and film uniformity of the composition may be improved.

The composition may be utilized to manufacture a light-emitting apparatus by a soluble process.

The composition may be provided by a soluble process on a substrate including an emission zone in which the first electrode and the second electrode are located.

The soluble process may be a spin coating method, a slit coating method, a drop casting method, a casting method, a gravure coating method, a bar coating method, a roll coating method, a dip coating method, a spray coating method, a screen coating method, a flexo printing method, an offset printing method, an inkjet printing method, or a nozzle printing method, but is not limited thereto.

In an embodiment, the soluble process may be performed by a spin coating method, a slit coating method, or an inkjet printing method, but embodiments of the present disclosure are not limited thereto.

In an embodiment, the composition may be provided in the form of a film on a substrate, in which the first electrode and the second electrode are located, by a spin coating method, or may be provided in the form of micro droplets, on the substrate by an inkjet printing method.

In the inkjet printing method, an inkjet printer having an inkjet head equipped with a piezo-type nozzle applying pressure according to a voltage may be utilized.

In more detail, the composition is ejected from a nozzle of an inkjet head onto a substrate.

In this regard, an amount of the quantum dot composition ejected may be from about 1 picoliter (pL) each time to about 50 pL each time, for example, from about 1 pL each time to about 30 pL each time, for example, from about 1 pL each time to about 20 pL each time.

An aperture of the inkjet head may be from about 5 micrometers (μm) to about 50 μm, for example, from about 10 μm to about 30 μm, to minimize clogging of the nozzle and improve ejection precision, but is not limited thereto.

Ejection pressure of the inkjet head may be from about 1,000 s⁻¹ to about 10,000 s⁻¹ based on the shear rate, but is not limited thereto.

Although a temperature during formation of a coating film is not particularly limited, in terms of suppressing crystallization of a material included in the composition, the temperature may be from about 10 C. ° to about 50 C. °, for example, from about 15 C. ° to about 40 C. °, for example, from about 15 C. ° to about 30 C. °, for example, from about 20 C. ° to about 25 C. °.

FIG. 3 is a schematic cross-sectional view of a light-emitting device 10 according to an embodiment of the disclosure. The light-emitting device 10 includes a first electrode 110, an interlayer 130, and a second electrode 150. Hereinafter, a structure of the light-emitting device 10 according to an embodiment and a method of manufacturing the light-emitting device 10 will be described in connection with FIG. 3.

In FIG. 3, a substrate (not shown) may be additionally located under the first electrode 110 or above the second electrode 150. As the substrate, a glass substrate or a plastic substrate may be used. In an embodiment, the substrate may be a flexible substrate, and may include plastics with excellent heat resistance and excellent durability, such as polyimide, polyethylene terephthalate (PET), polycarbonate, polyethylene napthalate, polyarylate (PAR), polyetherimide, or any combination thereof.

The first electrode 110 may be formed by, for example, depositing or sputtering a material for forming the first electrode 110 on the substrate. When the first electrode 110 is an anode, a material for forming the first electrode 110 may be a high work function material that facilitates injection of holes.

The first electrode 110 may be a reflective electrode, a semi-transmissive electrode, or a transmissive electrode. When the first electrode 110 is a transmissive electrode, a material for forming the first electrode 110 may include indium tin oxide (ITO), indium zinc oxide (IZO), tin oxide (SnO₂), zinc oxide (ZnO), or any combinations thereof.

In one or more embodiments, when the first electrode 110 is a semi-transmissive electrode or a reflective electrode, magnesium (Mg), silver (Ag), aluminum (AI), aluminum-lithium (Al—Li), calcium (Ca), magnesium-indium (Mg—In), magnesium-silver (Mg—Ag), or any combinations thereof may be used as a material for forming a first electrode.

The first electrode 110 may have a single-layered structure consisting of a single layer or a multilayer structure including a plurality of layers. In an embodiment, the first electrode 110 may have a three-layered structure of ITO/Ag/ITO.

The interlayer 130 may be located on the first electrode 110. The interlayer 130 may include an emission layer.

The interlayer 130 may further include a hole transport region between the first electrode 110 and the emission layer and an electron transport region between the emission layer and the second electrode 150.

The interlayer 130 may further include metal-containing compounds such as organometallic compounds, inorganic materials such as quantum dots, and the like, in addition to various organic materials.

In one or more embodiments, the interlayer 130 may include, i) two or more emission layers sequentially stacked between the first electrode 110 and the second electrode 150 and ii) a charge generation layer located between the two emission layers. When the interlayer 130 includes the emission layer and the charge generation layer as described above, the light-emitting device 10 may be a tandem light-emitting device.

Hole Transport Region of Interlayer 130

The hole transport region may have: i) a single-layered structure consisting of a single material, ii) a single-layered structure consisting of a plurality of different materials, or iii) a multi-layered structure including a plurality of layers including different materials in adjacent layers.

The hole transport region may include a hole injection layer, a hole transport layer, an emission auxiliary layer, an electron blocking layer, or any combination thereof.

In an embodiment, the hole transport region may have a multi-layered structure including a hole injection layer/hole transport layer structure, a hole injection layer/hole transport layer/emission auxiliary layer structure, a hole injection layer/emission auxiliary layer structure, or a hole injection layer/hole transport layer/electron blocking layer structure, wherein, in each structure, layers are stacked sequentially from the first electrode 110.

The hole transport region may include a compound represented by Formula 201, a compound represented by Formula 202, or any combination thereof:

wherein, in Formulae 201 and 202,

L₂₀₁ to L₂₀₄ may each independently be a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a) or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a),

L₂₀₅ may be *—O—*′, *—S—*′, *—N(Q₂₀₁)-*′, a C₁-C₂₀ alkylene group unsubstituted or substituted with at least one R_(10a), a C₂-C₂₀ alkenylene group unsubstituted or substituted with at least one R_(10a), a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a), or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a),

xa1 to xa4 may each independently be an integer from 0 to 5,

xa5 may be an integer from 1 to 10,

R₂₀₁ to R₂₀₄ and Q₂₀₁ may each independently be a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a) or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a),

R₂₀₁ and R₂₀₂ may optionally be linked to each other, via a single bond, a C₁-C₅ alkylene group unsubstituted or substituted with at least one R_(10a), or a C₂-C₅ alkenylene group unsubstituted or substituted with at least one R_(10a), to form a C₈-C₆₀ polycyclic group (for example, a carbazole group or the like) unsubstituted or substituted with at least one R_(10a),

R₂₀₃ and R₂₀₄ may optionally be linked to each other, via a single bond, a C₁-C₅ alkylene group unsubstituted or substituted with at least one R_(10a), or a C₂-C₅ alkenylene group unsubstituted or substituted with at least one R_(10a), to form a C₈-C₆₀ polycyclic group unsubstituted or substituted with at least one R_(10a), and

na1 may be an integer from 1 to 4.

In an embodiment, each of Formulae 201 and 202 may include at least one of groups represented by Formulae CY201 to CY217:

R_(10b) and R_(10c) in Formulae CY201 to CY217 are each the same as described in connection with R_(10a), ring CY₂₀₁ to ring CY₂₀₄ may each independently be a C₃-C₂₀ carbocyclic group or a C₁-C₂₀ heterocyclic group, and at least one hydrogen in Formulae CY201 to CY217 may be unsubstituted or substituted with R_(10a) as described above.

In an embodiment, ring CY₂₀₁ to ring CY₂₀₄ in Formulae CY201 to CY217 may each independently be a benzene group, a naphthalene group, a phenanthrene group, or an anthracene group.

In an embodiment, each of Formulae 201 and 202 may include at least one of groups represented by Formulae CY201 to CY203.

In an embodiment, Formula 201 may include at least one of groups represented by Formulae CY201 to CY203 and at least one of groups represented by Formulae CY204 to CY217.

In an embodiment, xa1 in Formula 201 may be 1, R₂₀₁ may be a group represented by one of Formulae CY201 to CY203, xa2 may be 0, and R₂₀₂ may be a group represented by one of Formulae CY204 to CY207.

In an embodiment, each of Formulae 201 and 202 may not include a group represented by one of Formulae CY201 to CY203.

In an embodiment, each of Formulae 201 and 202 may not include groups represented by Formulae CY201 to CY203, and may include at least one of groups represented by Formulae CY204 to CY217.

In an embodiment, each of Formulae 201 and 202 may not include groups represented by Formulae CY201 to CY217.

In an embodiment, the hole transport region may include a compound of Formula 201, a compound of Formula 202, m-MTDATA, TDATA, 2-TNATA, NPB (NPD), β-NPB, TPD, Spiro-TPD, Spiro-NPB, methylated NPB, TAPC, HMTPD, 4,4′, 4″-tris(N-carbazolyl)triphenylamine (TCTA), polyaniline/dodecylbenzenesulfonic acid (PANI/DBSA), poly(3,4-ethylenedioxythiophene)/poly(4-styrenesulfonate) (PEDOT/PSS), polyaniline/camphor sulfonic acid (PANI/CSA), polyaniline/poly(4-styrenesulfonate) (PANI/PSS), or any combination thereof.

A thickness of the hole transport region may be in a range of about 50 Å to about 10,000 Å, for example, about 100 Å to about 4,000 Å. When the hole transport region includes a hole injection layer, a hole transport layer, or any combination thereof, a thickness of the hole injection layer may be in a range of about 100 Å to about 9,000 Å, for example, about 100 Å to about 1,000 Å, and a thickness of the hole transport layer may be in a range of about 50 Å to about 2,000 Å, for example, about 100 Å to about 1,500 Å. When the thicknesses of the hole transport region, the hole injection layer, and the hole transport layer are within these ranges, satisfactory hole-transporting characteristics may be obtained without a substantial increase in driving voltage.

The emission auxiliary layer may increase light-emission efficiency by compensating for an optical resonance distance according to the wavelength of light emitted by an emission layer, and the electron blocking layer may block the injection of electrons from an electron transport region. The emission auxiliary layer and the electron blocking layer may include the materials as described above.

The hole transport region may further include, in addition to these materials, a charge-generation material for the improvement of conductive properties. The charge-generation material may be uniformly or non-uniformly dispersed in the hole transport region (for example, in the form of a single layer consisting of a charge-generation material).

The charge-generation material may be, for example, a p-dopant.

In an embodiment, a lowest unoccupied molecular orbital (LUMO) energy level of the p-dopant may be about −3.5 electron Volts (eV) or less.

In an embodiment, the p-dopant may include a quinone derivative, a cyano group-containing compound, a compound containing element EL1 and element EL2, or any combination thereof.

Examples of the quinone derivative may include TCNQ, F4-TCNQ, and the like.

Examples of the cyano group-containing compound may include HAT-CN, a compound represented by Formula 221 below, and the like.

In Formula 221,

R₂₂₁ to R₂₂₃ may each independently be a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a) or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a), and

at least one of R₂₂₁ to R₂₂₃ may each independently be: a C₃-C₆₀ carbocyclic group or a C₁-C₆₀ heterocyclic group, each substituted with: a cyano group; —F; —Cl; —Br; —I; a C₁-C₂₀ alkyl group substituted with a cyano group, —F, —Cl, —Br, —I, or any combination thereof; or any combination thereof.

In the compound containing element EL1 and element EL2, element EL1 may be metal, metalloid, or a combination thereof, and element EL2 may be non-metal, metalloid, or a combination thereof.

Examples of the metal may include: an alkali metal (for example, lithium (Li), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), etc.); an alkaline earth metal (for example, beryllium (Be), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), etc.); a transition metal (for example, titanium (Ti), zirconium (Zr), hafnium (Hf), vanadium (V), niobium (Nb), tantalum (Ta), chromium (Cr), molybdenum (Mo), tungsten (W), manganese (Mn), technetium (Tc), rhenium (Re), iron (Fe), ruthenium (Ru), osmium (Os), cobalt (Co), rhodium (Rh), iridium (Ir), nickel (Ni), palladium (Pd), platinum (Pt), copper (Cu), silver (Ag), gold (Au), etc.); a post-transition metal (for example, zinc (Zn), indium (In), tin (Sn), etc.); and a lanthanide metal (for example, lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), lutetium (Lu), etc.).

Examples of the metalloid may include silicon (Si), antimony (Sb), and tellurium (Te).

Examples of the non-metal may include oxygen (O) and halogen (for example, F, Cl, Br, I, etc.).

In an embodiment, examples of the compound containing element EL1 and element EL2 may include metal oxide, metal halide (for example, metal fluoride, metal chloride, metal bromide, or metal iodide), metalloid halide (for example, metalloid fluoride, metalloid chloride, metalloid bromide, or metalloid iodide), metal telluride, or any combination thereof.

Examples of the metal oxide may include tungsten oxide (for example, WO, W₂O₃, WO₂, WO₃, W₂O₅, etc.), vanadium oxide (for example, VO, V₂O₃, VO₂, V₂O₅, etc.), molybdenum oxide (MoO, Mo₂O₃, MoO₂, MoO₃, Mo₂O₅, etc.), and rhenium oxide (for example, ReO₃, etc.).

Examples of the metal halide may include alkali metal halide, alkaline earth metal halide, transition metal halide, post-transition metal halide, and lanthanide metal halide.

Examples of the alkali metal halide may include LiF, NaF, KF, RbF, CsF, LiCl, NaCl, KCl, RbCl, CsCl, LiBr, NaBr, KBr, RbBr, CsBr, LiI, NaI, KI, RbI, and CsI.

Examples of the alkaline earth metal halide may include BeF₂, MgF₂, CaF₂, SrF₂, BaF₂, BeCl₂, MgCl₂, CaCl₂), SrCl₂, BaCl₂, BeBr₂, MgBr₂, CaBr₂, SrBr₂, BaBr₂, BeI₂, MgI₂, CaI₂, SrI₂, and BaI₂.

Examples of the transition metal halide may include titanium halide (for example, TiF₄, TiCl₄, TiBr₄, TiI₄, etc.), zirconium halide (for example, ZrF₄, ZrCl₄, ZrBr₄, ZrI₄, etc.), hafnium halide (for example, HfF₄, HfCl₄, HfBr₄, HfI₄, etc.), vanadium halide (for example, VF₃, VCI₃, VBr₃, VI₃, etc.), niobium halide (for example, NbF₃, NbCl₃, NbBr₃, Nbl₃, etc.), tantalum halide (for example, TaF₃, TaCl₃, TaBr₃, Tal₃, etc.), chromium halide (for example, CrF₃, CrCl₃, CrBr₃, CrI₃, etc.), molybdenum halide (for example, MoF₃, MoCl₃, MoBr₃, MoI₃, etc.), tungsten halide (for example, WF₃, WCl₃, WBr₃, WI₃, etc.), manganese halide (for example, MnF₂, MnCl₂, MnBr₂, MnI₂, etc.), technetium halide (for example, TcF₂, TcCl₂, TcBr₂, Tci₂, etc.), rhenium halide (for example, ReF₂, ReCl₂, ReBr₂, ReI₂, etc.), iron halide (for example, FeF₂, FeCl₂, FeBr₂, FeI₂, etc.), ruthenium halide (for example, RuF₂, RuCl₂, RuBr₂, Rul₂, etc.), osmium halide (for example, OsF₂, OsCl₂, OsBr₂, OsI₂, etc.), cobalt halide (for example, CoF₂, COCl₂, CoBr₂, CoI₂, etc.), rhodium halide (for example, RhF₂, RhCl₂, RhBr₂, RhI₂, etc.), iridium halide (for example, IrF₂, IrCl₂, IrBr₂, IrI₂, etc.), nickel halide (for example, NiF₂, NiCl₂, NiBr₂, NiI₂, etc.), palladium halide (for example, PdF₂, PdCl₂, PdBr₂, PdI₂, etc.), platinum halide (for example, PtF₂, PtCl₂, PtBr₂, PtI₂, etc.), copper halide (for example, CuF, CuCl, CuBr, Cul, etc.), silver halide (for example, AgF, AgCl, AgBr, AgI, etc.), and gold halide (for example, AuF, AuCl, AuBr, AuI, etc.).

Examples of the post-transition metal halide may include zinc halide (for example, ZnF₂, ZnCl₂, ZnBr₂, ZnI₂, etc.), indium halide (for example, InI₃, etc.), and tin halide (for example, SnI₂, etc.).

Examples of the lanthanide metal halide may include YbF, YbF₂, YbF₃, SmF₃, YbCl, YbCl₂, YbCl₃ SmCl₃, YbBr, YbBr₂, YbBr₃, SmBr₃, YbI, YbI₂, YbI₃, and SmI₃.

Examples of the metalloid halide may include antimony halide (for example, SbCl₅, etc.).

Examples of the metal telluride may include alkali metal telluride (for example, Li₂Te, Na₂Te, K₂Te, Rb₂Te, Cs₂Te, etc.), alkaline earth metal telluride (for example, BeTe, MgTe, CaTe, SrTe, BaTe, etc.), transition metal telluride (for example, TiTe₂, ZrTe₂, HfTe₂, V₂Te₃, Nb₂Te₃, Ta₂Te₃, Cr₂Te₃, Mo₂Te₃, W₂Te₃, MnTe, TcTe, ReTe, FeTe, RuTe, OsTe, CoTe, RhTe, IrTe, NiTe, PdTe, PtTe, Cu₂Te, CuTe, Ag₂Te, AgTe, Au₂Te, etc.), post-transition metal telluride (for example, ZnTe, etc.), and lanthanide metal telluride (for example, LaTe, CeTe, PrTe, NdTe, PmTe, EuTe, GdTe, TbTe, DyTe, HoTe, ErTe, TmTe, YbTe, LuTe, etc.).

Emission Layer in Interlayer 130

When the light-emitting device 10 is a full-color light-emitting device, the emission layer may be patterned into a red emission layer, a green emission layer, and/or a blue emission layer, arranged as a sub-pixel. In an embodiment, the emission layer may have a stacked structure of two or more layers of a red emission layer, a green emission layer, and a blue emission layer, in which the two or more layers contact each other or are separated from each other. In one or more embodiments, the emission layer may include two or more materials of a red light-emitting material, a green light-emitting material, and a blue light-emitting material, in which the two or more materials are mixed with each other in a single layer to emit white light.

The emission layer may include a host and a dopant. The dopant may include a phosphorescent dopant, a fluorescent dopant, or any combination thereof.

An amount of the dopant in the emission layer may be from about 0.01 parts by weight to about 15 parts by weight based on 100 parts by weight of the host.

In an embodiment, the emission layer may include a quantum dot.

In an embodiment, the emission layer may include a delayed fluorescence material. The delayed fluorescence material may act as a host or a dopant in the emission layer.

A thickness of the emission layer may be in a range of about 100 Å to about 1,000 Å, for example, about 200 Å to about 600 Å. When the thickness of the emission layer is within the range, excellent light-emission characteristics may be obtained without a substantial increase in driving voltage.

Host

The host may include a compound represented by Formula 301 below:

[Ar₃₀₁]_(xb11)-[(L₃₀₁)_(xb1)-R₃₀₁]_(xb21)  Formula 301

wherein, in Formula 301,

Ar₃₀₁ and L₃₀₁ may each independently be a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a) or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a),

xb11 may be 1, 2, or 3,

xb1 may be an integer from 0 to 5,

R₃₀₁ may be hydrogen, deuterium, —F, —Cl, —Br, —I, a hydroxyl group, a cyano group, a nitro group, a C₁-C₆₀ alkyl group unsubstituted or substituted with at least one R_(10a), a C₂-C₆₀ alkenyl group unsubstituted or substituted with at least one R_(10a), a C₂-C₆₀ alkynyl group unsubstituted or substituted with at least one R_(10a), a C₁-C₆₀ alkoxy group unsubstituted or substituted with at least one R_(10a), a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a), a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a), —Si(Q₃₀₁)(Q₃₀₂)(Q₃₀₃), —N(Q₃₀₁)(Q₃₀₂), —B(Q₃₀₁)(Q₃₀₂), —C(═O)(Q₃₀₁), —S(═O)₂(Q₃₀₁), or —P(═O)(Q₃₀₁)(Q₃₀₂),

xb21 may be an integer from 1 to 5, and

Q₃₀₁ to Q₃₀₃ are each the same as described in connection with Q₁.

In an embodiment, when xb11 in Formula 301 is 2 or more, two or more of Ar₃₀₁(s) may be linked to each other via a single bond.

In an embodiment, the host may include a compound represented by Formula 301-1, a compound represented by Formula 301-2, or any combination thereof:

wherein, in Formulae 301-1 to 301-2,

ring A₃₀₁ to ring A₃₀₄ may each independently be a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a) or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a),

X₃₀₁ may be O, S, N-[(L₃₀₄)_(xb4)-R₃₀₄], C(R₃₀₄)(R₃₀₅), or Si(R₃₀₄)(R₃₀₅),

xb22 and xb23 may each independently be 0, 1, or 2,

L₃₀₁, xb1, and R₃₀₁ are each the same as described in the present specification,

L₃₀₂ to L₃₀₄ are each independently the same as described in connection with L₃₀₁,

xb2 to xb4 are each independently the same as described in connection with xb1, and

R₃₀₂ to R₃₀₅ and R₃₁₁ to R₃₁₄ are each the same as described in connection with R₃₀₁.

In an embodiment, the host may include an alkaline earth-metal complex. In an embodiment, the host may include a Be complex (for example, Compound H55), an Mg complex, a Zn complex, or a combination thereof.

In an embodiment, the host may include 9,10-di(2-naphthyl)anthracene (ADN), 2-methyl-9,10-bis(naphthalen-2-yl)anthracene (MADN), 9,10-di-(2-naphthyl)-2-t-butyl-anthracene (TBADN), 4,4′-bis(N-carbazolyl)-1,1′-biphenyl (CBP), 1,3-di-9-carbazolylbenzene (mCP), 1,3,5-tri(carbazol-9-yl)benzene (TCP), or any combination thereof.

Phosphorescent Dopant

The phosphorescent dopant may include at least one transition metal as a central metal. The phosphorescent dopant may include a monodentate ligand, a bidentate ligand, a tridentate ligand, a tetradentate ligand, a pentadentate ligand, a hexadentate ligand, or any combination thereof.

The phosphorescent dopant may be electrically neutral.

In an embodiment, the phosphorescent dopant may include an organometallic compound represented by Formula 401:

wherein, in Formulae 401 and 402,

M may be transition metal (for example, iridium (Ir), platinum (Pt), palladium (Pd), osmium (Os), titanium (Ti), gold (Au), hafnium (Hf), europium (Eu), terbium (Tb), rhodium (Rh), rhenium (Re), or thulium (Tm)),

L₄₀₁ may be a ligand represented by Formula 402, and xc1 may be 1, 2, or 3, wherein, when xc1 is two or more, two or more of L₄₀₁(s) may be identical to or different from each other,

L₄₀₂ may be an organic ligand, and xc2 may be 0, 1, 2, 3, or 4, wherein, when xc2 is 2 or more, two or more of L₄₀₂(s) may be identical to or different from each other,

X₄₀₁ and X₄₀₂ may each independently be nitrogen or carbon,

ring A₄₀₁ and ring A₄₀₂ may each independently be a C₃-C₆₀ carbocyclic group or a C₁-C₆₀ heterocyclic group,

T₄₀₁ may be a single bond, —O—, —S—, —C(═O)—, —N(Q₄₁₁)-, —C(Q₄₁₁)(Q₄₁₂)-, —C(Q₄₁₁)=C(Q₄₁₂)-, —C(Q₄₁₁)=, or ═C(Q₄₁₁)=,

X₄₀₃ and X₄₀₄ may each independently be a chemical bond (for example, a covalent bond or a coordinate bond), O, S, N(Q₄₁₃), B(Q₄₁₃), P(Q₄₁₃), C(Q₄₁₃)(Q₄₁₄), or Si(Q₄₁₃)(Q₄₁₄),

Q₄₁₁ to Q₄₁₄ are each the same as described in connection with Q₁,

R₄₀₁ and R₄₀₂ may each independently be hydrogen, deuterium, —F, —Cl, —Br, —I, a hydroxyl group, a cyano group, a nitro group, a C₁-C₂₀ alkyl group unsubstituted or substituted with at least one R_(10a), a C₁-C₂₀ alkoxy group unsubstituted or substituted with at least one R_(10a), a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a), a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a), —Si(Q₄₀₁)(Q₄₀₂)(Q₄₀₃), —N(Q₄₀₁)(Q₄₀₂), —B(Q₄₀₁)(Q₄₀₂), —C(═O)(Q₄₀₁), —S(═O)₂(Q₄₀₁), or —P(═O)(Q₄₀₁)(Q₄₀₂),

Q₄₀₁ to Q₄₀₃ are each the same as described in connection with Q₁,

xc11 and xc12 may each independently be an integer from 0 to 10, and

* and *′ in Formula 402 each indicate a binding site to M in Formula 401.

In an embodiment, in Formula 402, i) X₄₀₁ may be nitrogen, and X₄₀₂ may be carbon, or ii) each of X₄₀₁ and X₄₀₂ may be nitrogen.

In an embodiment, when xc1 in Formula 402 is 2 or more, two ring A₄₀₁ in two or more of L₄₀₁(s) may be optionally linked to each other via T₄₀₂, which is a linking group, and two ring A₄₀₂ may optionally be linked to each other via T₄₀₃, which is a linking group (see Compounds PD1 to PD4 and PD7). T₄₀₂ and T₄₀₃ are each the same as described in connection with T₄₀₁.

L₄₀₂ in Formula 401 may be an organic ligand. In an embodiment, L₄₀₂ may include a halogen group, a diketone group (for example, an acetylacetonate group), a carboxylic acid group (for example, a picolinate group), —C(═O), an isonitrile group, —CN group, a phosphorus group (for example, a phosphine group, a phosphite group, etc.), or any combination thereof.

Fluorescent Dopant

The fluorescent dopant may include an amine group-containing compound, a styryl group-containing compound, or any combination thereof.

In an embodiment, the fluorescent dopant may include a compound represented by Formula 501:

wherein, in Formula 501,

Ar₅₀₁, L₅₀₁ to L₅₀₃, R₅₀₁, and R₅₀₂ may each independently be a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a) or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a),

xd1 to xd3 may each independently be 0, 1, 2, or 3, and

xd4 may be 1, 2, 3, 4, 5, or 6.

In an embodiment, Ar₅₀₁ in Formula 501 may be a condensed cyclic group (for example, an anthracene group, a chrysene group, or a pyrene group) in which three or more monocyclic groups are condensed together.

In an embodiment, xd4 in Formula 501 may be 2.

In an embodiment, the fluorescent dopant may include DPVBi, DPAVBi, or any combination thereof.

Delayed Fluorescence Material

The emission layer may include a delayed fluorescence material.

In the present specification, the delayed fluorescence material may be selected from compounds capable of emitting delayed fluorescence based on a delayed fluorescence emission mechanism.

The delayed fluorescence material included in the emission layer may act as a host or a dopant depending on the type of other materials included in the emission layer.

In an embodiment, the difference between the triplet energy level (eV) of the delayed fluorescence material and the singlet energy level (eV) of the delayed fluorescence material may be greater than or equal to about 0 eV and less than or equal to about 0.5 eV. When the difference between the triplet energy level (eV) of the delayed fluorescence material and the singlet energy level (eV) of the delayed fluorescence material satisfies the above-described range, up-conversion from the triplet state to the singlet state of the delayed fluorescence materials may effectively occur, and thus, the luminescence efficiency of the light-emitting device 10 may be improved.

In an embodiment, the delayed fluorescence material may include i) a material including at least one electron donor (for example, a π electron-rich C₃-C₆₀ cyclic group, such as a carbazole group) and at least one electron acceptor (for example, a sulfoxide group, a cyano group, or a π electron-deficient nitrogen-containing C₁-C₆₀ cyclic group), and ii) a material including a C₈-C₆₀ polycyclic group in which two or more cyclic groups are condensed while sharing boron (B).

Quantum Dot

The emission layer may include a quantum dot.

In the present specification, a quantum dot refers to a crystal of a semiconductor compound, and may include any material capable of emitting light of various emission wavelengths according to the size of the crystal.

A diameter of the quantum dot may be, for example, in a range of about 1 nm to about 10 nm.

The quantum dot may be synthesized by a wet chemical process, a metal organic chemical vapor deposition process, a molecular beam epitaxy process, or any process similar thereto.

According to the wet chemical process, a precursor material is mixed with an organic solvent to grow a quantum dot particle crystal. When the crystal grows, the organic solvent naturally acts as a dispersant coordinated on the surface of the quantum dot crystal and controls the growth of the crystal so that the growth of quantum dot particles can be controlled through a process which is more easily performed than vapor deposition methods, such as metal organic chemical vapor deposition (MOCVD) or molecular beam epitaxy (MBE), and which requires low costs.

The quantum dot may include: a Group III-VI semiconductor compound; a Group II-VI semiconductor compound; a Group III-V semiconductor compound; a Group I-III-VI semiconductor compound; a Group IV-VI semiconductor compound; a Group IV element or compound; or any combination thereof.

Examples of the Group III-VI semiconductor compound may include: a binary compound such as In₂S₃, GaS, GaSe, Ga₂Se₃, GaTe, InS, InSe, In₂Se₃, or InTe; a ternary compound such as AgInS, AgInS₂, CuInS, CuInS₂, InGaS₃, InGaSe₃, or the like; or any combination thereof.

Examples of the Group II-VI semiconductor compound may include: a binary compound, such as CdSe, CdTe, ZnS, ZnSe, ZnTe, ZnO, HgS, HgSe, HgTe, MgSe, or MgS; a ternary compound, such as CdSeS, CdSeTe, CdSTe, ZnSeS, ZnSeTe, ZnSTe, HgSeS, HgSeTe, HgSTe, CdZnS, CdZnSe, CdZnTe, CdHgS, CdHgSe, CdHgTe, HgZnS, HgZnSe, HgZnTe, MgZnSe, or MgZnS; a quaternary compound, such as CdZnSeS, CdZnSeTe, CdZnSTe, CdHgSeS, CdHgSeTe, CdHgSTe, HgZnSeS, HgZnSeTe, or HgZnSTe; or any combination thereof.

Examples of the Group III-V semiconductor compound may include: a binary compound, such as GaN, GaP, GaAs, GaSb, AlN, AlP, AlAs, AlSb, InN, InP, InAs, InSb, or the like; a ternary compound, such as GaNP, GaNAs, GaNSb, GaPAs, GaPSb, AlNP, AlNAs, AlNSb, AlPAs, AlPSb, InGaP, InNP, InAlP, InNAs, InNSb, InPAs, InPSb, GaAlNP, or the like; a quaternary compound, such as GaAlNAs, GaAlNSb, GaAlPAs, GaAlPSb, GaInNP, GaInNAs, GaInNSb, GaInPAs, GaInPSb, InAlNP, InAlNAs, InAlNSb, InAlPAs, InAlPSb, or the like; or any combination thereof. In an embodiment, the Group III-V semiconductor compound may further include Group II elements. Examples of the Group III-V semiconductor compound further including Group II elements may include InZnP, InGaZnP, InAlZnP, and the like.

Examples of the Group I-III-VI semiconductor compound may include: a ternary compound, such as AgInS, AgInS₂, CuInS, CuInS₂, CuGaO₂, AgGaO₂, or AgAlO₂; or any combination thereof.

Examples of the Group IV-VI semiconductor compound may include: a binary compound, such as SnS, SnSe, SnTe, PbS, PbSe, PbTe, or the like; a ternary compound, such as SnSeS, SnSeTe, SnSTe, PbSeS, PbSeTe, PbSTe, SnPbS, SnPbSe, SnPbTe, or the like; a quaternary compound, such as SnPbSSe, SnPbSeTe, SnPbSTe, or the like; or any combination thereof.

The Group IV element or compound may include: a single element compound, such as Si or Ge; a binary compound, such as SiC or SiGe; or any combination thereof.

Each element included in a multi-element compound such as the binary compound, ternary compound, and quaternary compound, may exist in a particle with a uniform concentration or non-uniform concentration.

In an embodiment, the quantum dot may have a single structure or a dual core-shell structure. In the case of the quantum dot having a single structure, the concentration of each element included in the corresponding quantum dot is uniform. In an embodiment, the material contained in the core and the material contained in the shell may be different from each other.

The shell of the quantum dot may act as a protective layer to prevent chemical degeneration of the core to maintain semiconductor characteristics and/or as a charging layer to impart electrophoretic characteristics to the quantum dot. The shell may be a single layer or a multi-layer. The element presented in the interface between the core and the shell of the quantum dot may have a concentration gradient that decreases toward the center of the quantum dot.

Examples of the shell of the quantum dot may be an oxide of a metal or a non-metal, a semiconductor compound, and any combination thereof. Examples of the oxide of a metal or a non-metal may include: a binary compound, such as SiO₂, Al₂O₃, TiO₂, ZnO, MnO, Mn₂O₃, Mn₃O₄, CuO, FeO, Fe₂O₃, Fe₃O₄, CoO, CO₃O₄, or NiO; a ternary compound, such as MgAl₂O₄, CoFe₂O₄, NiFe₂O₄, or CoMn₂O₄; or any combination thereof.

Examples of the semiconductor compound may include, as described herein, a Group III-VI semiconductor compound, a Group II-VI semiconductor compound, a Group III-V semiconductor compound, a Group I-III-VI semiconductor compound, a Group IV-VI semiconductor compound, or any combination thereof. In addition, the semiconductor compound may include CdS, CdSe, CdTe, ZnS, ZnSe, ZnTe, ZnSeS, ZnTeS, GaAs, GaP, GaSb, HgS, HgSe, HgTe, InAs, InP, InGaP, InSb, AlAs, AlP, AlSb, or any combination thereof.

A full width at half maximum (FWHM) of an emission wavelength of the quantum dot may be about 45 nanometers (nm) or less, for example, about 40 nm or less, for example, about 30 nm or less, and within these ranges, color purity or color reproducibility may be improved. In addition, because the light emitted from the quantum dot is emitted in all directions a wide viewing angle can be enhanced.

In addition, the quantum dot may be a spherical particle, a pyramidal particle, a multi-arm particle, a cubic nanoparticle, a nanotube particle, a nanowire particle, a nanofiber particle, or a nanoplate particle.

Because the energy band gap can be adjusted by controlling the size of the quantum dot, light having various wavelength bands can be obtained from the quantum dot emission layer. Therefore, by using quantum dots of different sizes, a light-emitting device that emits light of various wavelengths may be implemented. In an embodiment, the size of the quantum dot may be selected to emit red, green and/or blue light. In addition, the size of the quantum dot may be configured to emit white light by combining light of the various colors.

The emission layer may be formed by the method of forming a quantum dot layer according to an embodiment of the disclosure.

Electron Transport Region of Interlayer 130

The electron transport region may have: i) a single-layered structure consisting of a single material, ii) a single-layered structure consisting of a plurality of different materials, or iii) a multi-layered structure including a plurality of layers including different materials of adjacent layers.

The electron transport region may include a hole blocking layer, an electron transport layer, an electron injection layer, or any combination thereof.

In an embodiment, the electron transport region may have an electron transport layer/electron injection layer structure or a hole blocking layer/electron transport layer/electron injection layer structure, wherein, in each structure, constituting layers are sequentially stacked from the emission layer.

The electron transport region (for example, the hole blocking layer or the electron transport layer in the electron transport region) may include a metal-free compound including at least one π electron-deficient nitrogen-containing C₁-C₆₀ cyclic group.

In an embodiment, the electron transport region may include a compound represented by Formula 601 below:

[Ar₆₀₁]_(xe11)-[(L₆₀₁)_(xe1)-R₆₀₁]_(xe21)  Formula 601

wherein, in Formula 601,

Ar₆₀₁ and L₆₀₁ may each independently be a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a) or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a),

xe11 may be 1, 2, or 3,

xe1 may be 0, 1, 2, 3, 4, or 5,

R₆₀₁ may be a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a), a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a), —Si(Q₆₀₁)(Q₆₀₂)(Q₆₀₃), —C(═O)(Q₆₀₁), —S(═O)₂(Q₆₀₁), or —P(═O)(Q₆₀₁)(Q₆₀₂),

Q₆₀₁ to Q₆₀₃ are each the same as described in connection with Q₁,

xe21 may be 1, 2, 3, 4, or 5, and

at least one of Ar₆₀₁, L₆₀₁, and R₆₀₁ may each independently be a π electron-deficient nitrogen-containing C₁-C₆₀ cyclic group unsubstituted or substituted with at least one R_(10a).

In an embodiment, when xe11 in Formula 601 is 2 or more, two or more of Ar₆₀₁(s) may be linked via a single bond.

In an embodiment, Ar₆₀₁ in Formula 601 may be a substituted or unsubstituted anthracene group.

In an embodiment, the electron transport region may include a compound represented by Formula 601-1:

wherein, in Formula 601-1,

X₆₁₄ may be N or C(R₆₁₄), X₆₁₅ may be N or C(R₆₁₅), X₆₁₆ may be N or C(R₆₁₆), at least one of X₆₁₄ to X₆₁₆ may be N,

L₆₁₁ to L₆₁₃ are each the same as described in connection with L₆₀₁,

xe611 to xe613 are each the same as described in connection with xe1,

R₆₁₁ to R₆₁₃ are each the same as described in connection with R₆₀₁, and

R₆₁₄ to R₆₁₆ may each independently be hydrogen, deuterium, —F, —Cl, —Br, —I, a hydroxyl group, a cyano group, a nitro group, a C₁-C₂₀ alkyl group, a C₁-C₂₀ alkoxy group, a C₃-C₆₀ carbocyclic group unsubstituted or substituted with at least one R_(10a), or a C₁-C₆₀ heterocyclic group unsubstituted or substituted with at least one R_(10a).

In an embodiment, xe1 and xe611 to xe613 in Formulae 601 and 601-1 may each independently be 0, 1, or 2.

The electron transport region may include 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline (BCP), 4,7-diphenyl-1,10-phenanthroline (Bphen), Alq₃, BAlq, TAZ, NTAZ, or any combination thereof.

The electron transport layer may be formed by the method of forming a quantum dot layer according to an embodiment of the disclosure.

A thickness of the electron transport region may be from about 160 Å to about 5,000 Å, for example, from about 100 Å to about 4,000 Å. When the electron transport region includes a hole blocking layer, an electron transport layer, or any combination thereof, thicknesses of the hole blocking layer and the electron transport layer may each independently be from about 20 Å to about 1,000 Å, for example, from about 30 Å to about 300 Å, and a thickness of the electron transport layer may be from about 100 Å to about 1,000 Å, for example, from about 150 Å to about 500 Å. When the thicknesses of the hole blocking layer and/or electron transport layer are within the ranges described above, satisfactory electron-transporting characteristics may be obtained without a substantial increase in driving voltage.

The electron transport region (for example, the electron transport layer in the electron transport region) may further include, in addition to the materials described above, a metal-containing material.

The metal-containing material may include an alkali metal complex, an alkaline earth metal complex, or any combination thereof. A metal ion of the alkali metal complex may be a Li ion, a Na ion, a K ion, a Rb ion, or a Cs ion, and a metal ion of the alkaline earth metal complex may be a Be ion, a Mg ion, a Ca ion, a Sr ion, or a Ba ion. A ligand coordinated with the metal ion of the alkali metal complex or the alkaline earth-metal complex may include a hydroxyquinoline, a hydroxyisoquinoline, a hydroxybenzoquinoline, a hydroxyacridine, a hydroxyphenanthridine, a hydroxyphenyloxazole, a hydroxyphenylthiazole, a hydroxydiphenyloxadiazole, a hydroxydiphenylthiadiazole, a hydroxyphenylpyridine, a hydroxyphenylbenzimidazole, a hydroxyphenylbenzothiazole, a bipyridine, a phenanthroline, a cyclopentadiene, or any combination thereof.

In an embodiment, the metal-containing material may include a Li complex. The Li complex may include, for example, Compound ET-D1 (LiQ) or ET-D2:

The electron transport region may include an electron injection layer that facilitates the injection of electrons from the second electrode 150. The electron injection layer may be in direct contact with the second electrode 150.

The electron injection layer may have: i) a single-layered structure consisting of a single material, ii) a single-layered structure consisting of a plurality of different materials, or iii) a multi-layered structure including a plurality of layers including different materials of adjacent layers.

The electron injection layer may include an alkali metal, an alkaline earth metal, a rare earth metal, an alkali metal-containing compound, an alkaline earth metal-containing compound, a rare earth metal-containing compound, an alkali metal complex, an alkaline earth metal complex, a rare earth metal complex, or any combination thereof.

The alkali metal may include Li, Na, K, Rb, Cs, or any combination thereof. The alkaline earth metal may include Mg, Ca, Sr, Ba, or any combination thereof. The rare earth metal may include Sc, Y, Ce, Tb, Yb, Gd, or any combination thereof.

The alkali metal-containing compound, the alkaline earth metal-containing compound, and the rare earth metal-containing compound may include oxides, halides (for example, fluorides, chlorides, bromides, or iodides), or tellurides of the alkali metal, the alkaline earth metal, and the rare earth metal, or any combination thereof.

The alkali metal-containing compound may include alkali metal oxides, such as Li₂O, Cs₂O, or K₂O, alkali metal halides, such as LiF, NaF, CsF, KF, LiI, NaI, CsI, or KI, or any combination thereof. The alkaline earth metal-containing compound may include an alkaline earth metal compound, such as BaO, SrO, CaO, Ba_(x)Sr_(1-x)O (x is a real number satisfying the condition of 0<x<1), Ba_(x)Ca_(1-x)O (x is a real number satisfying the condition of 0<x<1), or the like. The rare earth metal-containing compound may include YbF₃, ScF₃, Sc₂O₃, Y₂O₃, Ce₂O₃, GdF₃, TbF₃, YbI₃, ScI₃, Tbl₃, or any combination thereof. In an embodiment, the rare earth metal-containing compound may include lanthanide metal telluride. Examples of the lanthanide metal telluride may include LaTe, CeTe, PrTe, NdTe, PmTe, SmTe, EuTe, GdTe, TbTe, DyTe, HoTe, ErTe, TmTe, YbTe, LuTe, La₂Te₃, Ce₂Te₃, Pr₂Te₃, Nd₂Te₃, Pm₂Te₃, Sm₂Te₃, Eu₂Te₃, Gd₂Te₃, Tb₂Te₃, Dy₂Te₃, Ho₂Te₃, Er₂Te₃, Tm₂Te₃, Yb₂Te₃, and Lu₂Te₃.

The alkali metal complex, the alkaline earth-metal complex, and the rare earth metal complex may include i) one of ions of the alkali metal, the alkaline earth metal, and the rare earth metal and ii), as a ligand bonded to the metal ion, for example, a hydroxyquinoline, a hydroxyisoquinoline, a hydroxybenzoquinoline, a hydroxyacridine, a hydroxyphenanthridine, a hydroxyphenyloxazole, a hydroxyphenylthiazole, a hydroxydiphenyloxadiazole, a hydroxydiphenylthiadiazole, a hydroxyphenylpyridine, a hydroxyphenyl benzimidazole, a hydroxyphenylbenzothiazole, a bipyridine, a phenanthroline, a cyclopentadiene, or any combination thereof.

The electron injection layer may consist of an alkali metal, an alkaline earth metal, a rare earth metal, an alkali metal-containing compound, an alkaline earth metal-containing compound, a rare earth metal-containing compound, an alkali metal complex, an alkaline earth metal complex, a rare earth metal complex, or any combination thereof, as described above. In an embodiment, the electron injection layer may further include an organic material (for example, a compound represented by Formula 601).

In an embodiment, the electron injection layer may consist of i) an alkali metal-containing compound (for example, an alkali metal halide), ii) a) an alkali metal-containing compound (for example, an alkali metal halide); and b) an alkali metal, an alkaline earth metal, a rare earth metal, or any combination thereof. In an embodiment, the electron injection layer may be a KI:Yb co-deposited layer, an RbI:Yb co-deposited layer, or the like.

When the electron injection layer further includes an organic material, alkali metal, alkaline earth metal, rare earth metal, an alkali metal-containing compound, an alkaline earth metal-containing compound, a rare earth metal-containing compound, alkali metal complex, alkaline earth-metal complex, rare earth metal complex, or any combination thereof may be homogeneously or non-homogeneously dispersed in a matrix including the organic material.

A thickness of the electron injection layer may be in a range of about 1 Å to about 100 Å, and, for example, about 3 Å to about 90 Å. When the thickness of the electron injection layer is within the range described above, satisfactory electron injection characteristics may be obtained without a substantial increase in driving voltage.

The second electrode 150 may be located on the interlayer 130 having such a structure. The second electrode 150 may be a cathode, which is an electron injection electrode, and as the material for the second electrode 150, a metal, an alloy, an electrically conductive compound, or any combination thereof, each having a low work function, may be used.

In an embodiment, the second electrode 150 may include lithium (Li), silver (Ag), magnesium (Mg), aluminum (Al), aluminum-lithium (Al—Li), calcium (Ca), magnesium-indium (Mg—In), magnesium-silver (Mg—Ag), ytterbium (Yb), silver-ytterbium (Ag—Yb), ITO, IZO, or a combination thereof. The second electrode 150 may be a transmissive electrode, a semi-transmissive electrode, or a reflective electrode.

The second electrode 150 may have a single-layered structure or a multi-layered structure including two or more layers.

A first capping layer (not shown) may be located outside the first electrode 110, and/or a second capping layer (not shown) may be located outside the second electrode 150. In detail, the light-emitting device 10 may have a structure in which the first capping layer, the first electrode 110, the interlayer 130, and the second electrode 150 are sequentially stacked in this stated order, a structure in which the first electrode 110, the interlayer 130, the second electrode 150, and the second capping layer are sequentially stacked in this stated order, or a structure in which the first capping layer, the first electrode 110, the interlayer 130, the second electrode 150, and the second capping layer are sequentially stacked in this stated order.

Light generated in an emission layer of the interlayer 130 of the light-emitting device 10 may be extracted toward the outside through the first electrode 110, which is a semi-transmissive electrode or a transmissive electrode, and the first capping layer or light generated in an emission layer of the interlayer 130 of the light-emitting device 10 may be extracted toward the outside through the second electrode 150, which is a semi-transmissive electrode or a transmissive electrode, and the second capping layer.

The first capping layer and the second capping layer may increase external emission efficiency according to the principle of constructive interference. Accordingly, the light extraction efficiency of the light-emitting device 10 is increased, so that the emission efficiency of the light-emitting device 10 may be improved.

Each of the first capping layer and second capping layer may include a material having a refractive index (at 589 nm) of 1.6 or more.

The first capping layer or the second capping layer may each independently be an organic capping layer including an organic material, an inorganic capping layer including an inorganic material, or a composite capping layer including an organic material and an inorganic material.

At least one of the first capping layer or the second capping layer may each independently include carbocyclic compounds, heterocyclic compounds, amine group-containing compounds, porphyrin derivatives, phthalocyanine derivatives, naphthyllcyanine derivatives, alkali metal complexes, alkaline earth metal complexes, or any combination thereof. The carbocyclic compound, the heterocyclic compound, and the amine group-containing compound may be optionally substituted with a substituent containing O, N, S, Se, Si, F, Cl, Br, I, or any combination thereof. In an embodiment, at least one of the first capping layer and the second capping layer may each independently include an amine group-containing compound.

In an embodiment, at least one of the first capping layer or the second capping layer may each independently include a compound represented by Formula 201, a compound represented by Formula 202, or any combination thereof.

In an embodiment, at least one of the first capping layer or the second capping layer may each independently include one of Compounds HT28 to HT33, one of Compounds CP1 to CP6, β-NPB, or any combination thereof:

The light-emitting device may be included in various electronic apparatuses. In an embodiment, the electronic apparatus including a light-emitting device may be a light-emitting apparatus, an authentication apparatus, or the like.

The electronic apparatus (for example, light-emitting apparatus) may further include, in addition to the light-emitting device, i) a color filter, ii) a color conversion layer, or iii) a color filter and a color conversion layer. The color filter and/or the color conversion layer may be located in at least one traveling direction of light emitted from the light-emitting device. In an embodiment, the light emitted from the light-emitting device may be blue light or white light. The light-emitting device may be the same as described above. In an embodiment, the color conversion layer may include quantum dots. The quantum dot may be, for example, a quantum dot as described herein.

The electronic apparatus may include a first substrate. The first substrate may include a plurality of subpixel areas, the color filter may include a plurality of color filter areas respectively corresponding to the subpixel areas, and the color conversion layer may include a plurality of color conversion areas respectively corresponding to the subpixel areas.

A pixel-defining film may be located among the subpixel areas to define each of the subpixel areas.

The color filter may further include a plurality of color filter areas and light-shielding patterns located among the color filter areas, and the color conversion layer may include a plurality of color conversion areas and light-shielding patterns located among the color conversion areas.

The color filter areas (or the color conversion areas) may include a first area emitting first color light, a second area emitting second color light, and/or a third area emitting third color light, and the first color light, the second color light, and/or the third color light may have different maximum emission wavelengths from one another. In an embodiment, the first color light may be red light, the second color light may be green light, and the third color light may be blue light. In an embodiment, the color filter areas (or the color conversion areas) may include quantum dots. In detail, the first area may include a red quantum dot, the second area may include a green quantum dot, and the third area may not include a quantum dot. The quantum dot is the same as described in the present specification. The first area, the second area, and/or the third area may each include a scatterer.

In an embodiment, the light-emitting device may emit a source light, the first area may absorb the source light to emit a first color light, the second area may absorb the source light to emit a second color light, and the third area may absorb the source light to emit a third color light. In this regard, the first color light, the second color light, and the third color light may have different maximum emission wavelengths. In detail, the source light may be blue light, the first color light may be red light, the second color light may be green light, and the third color light may be blue light.

The electronic apparatus may further include a thin-film transistor in addition to the light-emitting device as described above. The thin-film transistor may include a source electrode, a drain electrode, and an activation layer, wherein any one of the source electrode and the drain electrode may be electrically connected to any one of the first electrode and the second electrode of the light-emitting device.

The thin-film transistor may further include a gate electrode, a gate insulating film, etc.

The activation layer may include crystalline silicon, amorphous silicon, organic semiconductor, oxide semiconductor, or the like.

The electronic apparatus may further include a sealing portion for sealing the light-emitting device. The sealing portion and/or the color conversion layer may be located between the color filter and the light-emitting device. The sealing portion may facilitate light from the light-emitting device to be transmitted to the outside, while simultaneously preventing ambient air and moisture from penetrating into the light-emitting device. The sealing portion may be a sealing substrate including a transparent glass substrate or a plastic substrate. The sealing portion may be a thin-film encapsulation layer including at least one layer of an organic layer and/or an inorganic layer. When the sealing portion is a thin film encapsulation layer, the electronic apparatus may be flexible.

Various functional layers may be additionally located on the sealing portion, in addition to the color filter and/or the color conversion layer, according to the use of the electronic apparatus. The functional layers may include a touch screen layer, a polarizing layer, and the like. The touch screen layer may be a pressure-sensitive touch screen layer, a capacitive touch screen layer, or an infrared touch screen layer. The authentication apparatus may be, for example, a biometric authentication apparatus that authenticates an individual by using biometric information of a living body (for example, fingertips, pupils, etc.).

The authentication apparatus may further include, in addition to the light-emitting device, a biometric information collector.

The electronic apparatus may be applied to various displays, light sources, lighting, personal computers (for example, a mobile personal computer), mobile phones, digital cameras, electronic diaries, electronic dictionaries, electronic game machines, medical instruments (for example, electronic thermometers, sphygmomanometers, blood glucose meters, pulse measurement devices, pulse wave measurement devices, electrocardiogram displays, ultrasonic diagnostic devices, or endoscope displays), fish finders, various measuring instruments, meters (for example, meters for a vehicle, an aircraft, and a vessel), projectors, and the like.

DEFINITION OF TERMS

The term “C₃-C₆₀ carbocyclic group” as used herein refers to a cyclic group consisting of carbon only and having three to sixty carbon atoms, and the term “C₁-C₆₀ heterocyclic group” as used herein refers to a cyclic group that has one to sixty carbon atoms and further has a heteroatom, in addition to carbon. The C₃-C₆₀ carbocyclic group and the C₁-C₆₀ heterocyclic group may each be a monocyclic group consisting of one ring or a polycyclic group in which two or more rings are condensed with each other. In an embodiment, the C₁-C₆₀ heterocyclic group has 3 to 61 ring-forming atoms.

The “cyclic group” as used herein may include the C₃-C₆₀ carbocyclic group and the C₁-C₆₀ heterocyclic group.

The term “π electron-rich C₃-C₆₀ cyclic group” as used herein refers to a cyclic group that has three to sixty carbon atoms and does not include *—N=*′ as a ring-forming moiety, and the term “π electron-deficient nitrogen-containing C₁-C₆₀ cyclic group” as used herein refers to a heterocyclic group that has one to sixty carbon atoms and includes *—N=*′ as a ring-forming moiety.

In an embodiment, the C₃-C₆₀ carbocyclic group may be i) group T1 or ii) a condensed cyclic group in which two or more groups T1 are condensed with each other (for example, a cyclopentadiene group, an adamantane group, a norbornane group, a benzene group, a pentalene group, a naphthalene group, an azulene group, an indacene group, an acenaphthylene group, a phenalene group, a phenanthrene group, an anthracene group, a fluoranthene group, a triphenylene group, a pyrene group, a chrysene group, a perylene group, a pentaphene group, a heptalene group, a naphthacene group, a picene group, a hexacene group, a pentacene group, a rubicene group, a coronene group, an ovalene group, an indene group, a fluorene group, a spiro-bifluorene group, a benzofluorene group, an indenophenanthrene group, or an indenoanthracene group),

the C₁-C₆₀ heterocyclic group may be i) group T2, ii) a condensed cyclic group in which two or more groups T2 are condensed with each other, or iii) a condensed cyclic group in which at least one group T2 and at least one group T1 are condensed with each other (for example, a pyrrole group, a thiophene group, a furan group, an indole group, a benzoindole group, a naphthoindole group, an isoindole group, a benzoisoindole group, a naphthoisoindole group, a benzosilole group, a benzothiophene group, a benzofuran group, a carbazole group, a dibenzosilole group, a dibenzothiophene group, a dibenzofuran group, an indenocarbazole group, an indolocarbazole group, a benzofurocarbazole group, a benzothienocarbazole group, a benzosilolocarbazole group, a benzoindolocarbazole group, a benzocarbazole group, a benzonaphthofuran group, a benzonaphthothiophene group, a benzonaphthosilole group, a benzofurodibenzofuran group, a benzofurodibenzothiophene group, a benzothienodibenzothiophene group, a pyrazole group, an imidazole group, a triazole group, an oxazole group, an isoxazole group, an oxadiazole group, a thiazole group, an isothiazole group, a thiadiazole group, a benzopyrazole group, a benzimidazole group, a benzoxazole group, a benzoisoxazole group, a benzothiazole group, a benzoisothiazole group, a pyridine group, a pyrimidine group, a pyrazine group, a pyridazine group, a triazine group, a quinoline group, an isoquinoline group, a benzoquinoline group, a benzoisoquinoline group, a quinoxaline group, a benzoquinoxaline group, a quinazoline group, a benzoquinazoline group, a phenanthroline group, a cinnoline group, a phthalazine group, a naphthyridine group, an imidazopyridine group, an imidazopyrimidine group, an imidazotriazine group, an imidazopyrazine group, an imidazopyridazine group, an azacarbazole group, an azafluorene group, an azadibenzosilole group, an azadibenzothiophene group, an azadibenzofuran group, etc.),

the π electron-rich C₃-C₆₀ cyclic group may be i) group T1, ii) a condensed cyclic group in which two or more groups T1 are condensed with each other, iii) group T3, iv) a condensed cyclic group in which two or more groups T3 are condensed with each other, or v) a condensed cyclic group in which at least one group T3 and at least one group T1 are condensed with each other (for example, the C₃-C₆₀ carbocyclic group, a pyrrole group, a thiophene group, a furan group, an indole group, a benzoindole group, a naphthoindole group, an isoindole group, a benzoisoindole group, a naphthoisoindole group, a benzosilole group, a benzothiophene group, a benzofuran group, a carbazole group, a dibenzosilole group, a dibenzothiophene group, a dibenzofuran group, an indenocarbazole group, an indolocarbazole group, a benzofurocarbazole group, a benzothienocarbazole group, a benzosilolocarbazole group, a benzoindolocarbazole group, a benzocarbazole group, a benzonaphthofuran group, a benzonaphthothiophene group, a benzonaphthosilole group, a benzofurodibenzofuran group, a benzofurodibenzothiophene group, a benzothienodibenzothiophene group, etc.),

the π electron-deficient nitrogen-containing C₁-C₆₀ cyclic group may be i) group T4, ii) a condensed cyclic group in which two or more group T4 are condensed with each other, iii) a condensed cyclic group in which at least one group T4 and at least one group T1 are condensed with each other, iv) a condensed cyclic group in which at least one group T4 and at least one group T3 are condensed with each other, or v) a condensed cyclic group in which at least one group T4, at least one group T1, and at least one group T3 are condensed with one another (for example, a pyrazole group, an imidazole group, a triazole group, an oxazole group, an isoxazole group, an oxadiazole group, a thiazole group, an isothiazole group, a thiadiazole group, a benzopyrazole group, a benzimidazole group, a benzoxazole group, a benzoisoxazole group, a benzothiazole group, a benzoisothiazole group, a pyridine group, a pyrimidine group, a pyrazine group, a pyridazine group, a triazine group, a quinoline group, an isoquinoline group, a benzoquinoline group, a benzoisoquinoline group, a quinoxaline group, a benzoquinoxaline group, a quinazoline group, a benzoquinazoline group, a phenanthroline group, a cinnoline group, a phthalazine group, a naphthyridine group, an imidazopyridine group, an imidazopyrimidine group, an imidazotriazine group, an imidazopyrazine group, an imidazopyridazine group, an azacarbazole group, an azafluorene group, an azadibenzosilole group, an azadibenzothiophene group, an azadibenzofuran group, etc.),

group T1 may be a cyclopropane group, a cyclobutane group, a cyclopentane group, a cyclohexane group, a cycloheptane group, a cyclooctane group, a cyclobutene group, a cyclopentene group, a cyclopentadiene group, a cyclohexene group, a cyclohexadiene group, a cycloheptene group, an adamantane group, a norbornane (or a bicyclo[2.2.1]heptane) group, a norbornene group, a bicyclo[1.1.1]pentane group, a bicyclo[2.1.1]hexane group, a bicyclo[2.2.2]octane group, or a benzene group,

group T2 may be a furan group, a thiophene group, a 1H-pyrrole group, a silole group, a borole group, a 2H-pyrrole group, a 3H-pyrrole group, an imidazole group, a pyrazole group, a triazole group, a tetrazole group, an oxazole group, an isoxazole group, an oxadiazole group, a thiazole group, an isothiazole group, a thiadiazole group, an azasilole group, an azaborole group, a pyridine group, a pyrimidine group, a pyrazine group, a pyridazine group, a triazine group, or a tetrazine group,

group T3 may be a furan group, a thiophene group, a 1H-pyrrole group, a silole group, or a borole group, and

group T4 may be a 2H-pyrrole group, a 3H-pyrrole group, an imidazole group, a pyrazole group, a triazole group, a tetrazole group, an oxazole group, an isoxazole group, an oxadiazole group, a thiazole group, an isothiazole group, a thiadiazole group, an azasilole group, an azaborole group, a pyridine group, a pyrimidine group, a pyrazine group, a pyridazine group, a triazine group, or a tetrazine group.

The term “cyclic group”, “C₃-C₆₀ carbocyclic group”, “C₁-C₆₀ heterocyclic group”, “π electron-rich C₃-C₆₀ cyclic group”, or “π electron-deficient nitrogen-containing C₁-C₆₀ cyclic group” as used herein refers to a group condensed to any cyclic group or a polyvalent group (for example, a divalent group, a trivalent group, a tetravalent group, etc.), depending on the structure of a formula in connection with which the terms are used. In an embodiment, “a benzene group” may be a benzo group, a phenyl group, a phenylene group, or the like, which may be easily understood by one of ordinary skill in the art according to the structure of a formula including the “benzene group.”

Examples of the monovalent C₃-C₆₀ carbocyclic group and the monovalent C₁-C₆₀ heterocyclic group may include a C₃-C₁₀ cycloalkyl group, a C₁-C₁₀ heterocycloalkyl group, a C₃-C₁₀ cycloalkenyl group, a C₁-C₁₀ heterocycloalkenyl group, a C₆-C₆₀ aryl group, a C₁-C₆₀ heteroaryl group, a monovalent non-aromatic condensed polycyclic group, and a monovalent non-aromatic condensed heteropolycyclic group, and examples of the divalent C₃-C₆₀ carbocyclic group and the divalent C₁-C₆₀ heterocyclic group may include a C₃-C₁₀ cycloalkylene group, a C₁-C₁₀ heterocycloalkylene group, a C₃-C₁₀ cycloalkenylene group, a C₁-C₁₀ heterocycloalkenylene group, a C₆-C₆₀ arylene group, a C₁-C₆₀ heteroarylene group, a divalent non-aromatic condensed polycyclic group, and a substituted or unsubstituted divalent non-aromatic condensed heteropolycyclic group.

The term “C₁-C₆₀ alkyl group” as used herein refers to a linear or branched aliphatic hydrocarbon monovalent group that has one to sixty carbon atoms, and examples thereof include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, a sec-butyl group, an isobutyl group, a tert-butyl group, an n-pentyl group, a tert-pentyl group, a neopentyl group, an isopentyl group, a sec-pentyl group, a 3-pentyl group, a sec-isopentyl group, an n-hexyl group, an isohexyl group, a sec-hexyl group, a tert-hexyl group, an n-heptyl group, an isoheptyl group, a sec-heptyl group, a tert-heptyl group, an n-octyl group, an isooctyl group, a sec-octyl group, a tert-octyl group, an n-nonyl group, an isononyl group, a sec-nonyl group, a tert-nonyl group, an n-decyl group, an isodecyl group, a sec-decyl group, and a tert-decyl group. The term “C₁-C₆₀ alkylene group” as used herein refers to a divalent group having the same structure as the C₁-C₆₀ alkyl group.

The term “C₂-C₆₀ alkenyl group” as used herein refers to a monovalent hydrocarbon group having at least one carbon-carbon double bond in the middle or at the terminus of the C₂-C₆₀ alkyl group, and examples thereof include an ethenyl group, a propenyl group, and a butenyl group. The term “C₂-C₆₀ alkenylene group” as used herein refers to a divalent group having the same structure as the C₂-C₆₀ alkenyl group.

The term “C₂-C₆₀ alkynyl group” as used herein refers to a monovalent hydrocarbon group having at least one carbon-carbon triple bond in the middle or at the terminus of the C₂-C₆₀ alkyl group, and examples thereof include an ethynyl group and a propynyl group. The term “C₂-C₆₀ alkynylene group” as used herein refers to a divalent group having the same structure as the C₂-C₆₀ alkynyl group.

The term “C₁-C₆₀ alkoxy group” as used herein refers to a monovalent group represented by —OA₁₀₁ (wherein A₁₀₁ is the C₁-C₆₀ alkyl group), and examples thereof include a methoxy group, an ethoxy group, and an isopropyloxy group.

The term “C₃-C₁₀ cycloalkyl group” as used herein refers to a monovalent saturated hydrocarbon cyclic group having 3 to 10 carbon atoms, and examples thereof include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, an adamantanyl group, a norbornanyl group (or a bicyclo[2.2.1]heptyl group), a bicyclo[1.1.1]pentyl group, a bicyclo[2.1.1]hexyl group, and a bicyclo[2.2.2]octyl group. The term “C₃-C₁₀ cycloalkylene group” as used herein refers to a divalent group having the same structure as the C₃-C₁₀ cycloalkyl group.

The term “C₁-C₁₀ heterocycloalkyl group” as used herein refers to a monovalent cyclic group that further includes, in addition to a carbon atom, at least one heteroatom as a ring-forming atom and has 1 to 10 carbon atoms, and examples thereof include a 1,2,3,4-oxatriazolidinyl group, a tetrahydrofuranyl group, and a tetrahydrothiophenyl group. The term “C₁-C₁₀ heterocycloalkylene group” as used herein refers to a divalent group having the same structure as the C₁-C₁₀ heterocycloalkyl group.

The term “C₃-C₁₀ cycloalkenyl group” used herein refers to a monovalent cyclic group that has three to ten carbon atoms and at least one carbon-carbon double bond in the ring thereof and no aromaticity, and examples thereof include a cyclopentenyl group, a cyclohexenyl group, and a cycloheptenyl group. The term “C₃-C₁₀ cycloalkenylene group” as used herein refers to a divalent group having the same structure as the C₃-C₁₀ cycloalkenyl group.

The term “C₁-C₁₀ heterocycloalkenyl group” as used herein refers to a monovalent cyclic group that has, in addition to a carbon atom, at least one heteroatom as a ring-forming atom, 1 to 10 carbon atoms, and at least one carbon-carbon double bond in the cyclic structure thereof. Examples of the C₁-C₁₀ heterocycloalkenyl group include a 4,5-dihydro-1,2,3,4-oxatriazolyl group, a 2,3-dihydrofuranyl group, and a 2,3-dihydrothiophenyl group. The term “C₁-C₁₀ heterocycloalkenylene group” as used herein refers to a divalent group having the same structure as the C₁-C₁₀ heterocycloalkenyl group.

The term “C₆-C₆₀ aryl group” as used herein refers to a monovalent group having a carbocyclic aromatic system having six to sixty carbon atoms, and the term “C₆-C₆₀ arylene group” as used herein refers to a divalent group having a carbocyclic aromatic system having six to sixty carbon atoms. Examples of the C₆-C₆₀ aryl group include a phenyl group, a pentalenyl group, a naphthyl group, an azulenyl group, an indacenyl group, an acenaphthyl group, a phenalenyl group, a phenanthrenyl group, an anthracenyl group, a fluoranthenyl group, a triphenylenyl group, a pyrenyl group, a chrysenyl group, a perylenyl group, a pentaphenyl group, a heptalenyl group, a naphthacenyl group, a picenyl group, a hexacenyl group, a pentacenyl group, a rubicenyl group, a coronenyl group, and an ovalenyl group. When the C₆-C₆₀ aryl group and the C₆-C₆₀ arylene group each include two or more rings, the rings may be condensed with each other.

The term “C₁-C₆₀ heteroaryl group” as used herein refers to a monovalent group having a heterocyclic aromatic system that has, in addition to a carbon atom, at least one heteroatom as a ring-forming atom, and 1 to 60 carbon atoms. The term “C₁-C₆₀ heteroarylene group” as used herein refers to a divalent group having a heterocyclic aromatic system that has, in addition to a carbon atom, at least one heteroatom as a ring-forming atom, and 1 to 60 carbon atoms. Examples of the C₁-C₆₀ heteroaryl group include a pyridinyl group, a pyrimidinyl group, a pyrazinyl group, a pyridazinyl group, a triazinyl group, a quinolinyl group, a benzoquinolinyl group, an isoquinolinyl group, a benzoisoquinolinyl group, a quinoxalinyl group, a benzoquinoxalinyl group, a quinazolinyl group, a benzoquinazolinyl group, a cinnolinyl group, a phenanthrolinyl group, a phthalazinyl group, and a naphthyridinyl group. When the C₁-C₆₀ heteroaryl group and the C₁-C₆₀ heteroarylene group each include two or more rings, the rings may be condensed with each other.

The term “monovalent non-aromatic condensed polycyclic group” as used herein refers to a monovalent group having two or more rings condensed to each other, only carbon atoms (for example, having 8 to 60 carbon atoms) as ring-forming atoms, and non-aromaticity in its molecular structure when considered as a whole. Examples of the monovalent non-aromatic condensed polycyclic group include an indenyl group, a fluorenyl group, a spiro-bifluorenyl group, a benzofluorenyl group, an indenophenanthrenyl group, and an indeno anthracenyl group. The term “divalent non-aromatic condensed polycyclic group” as used herein refers to a divalent group having the same structure as a monovalent non-aromatic condensed polycyclic group.

The term “monovalent non-aromatic condensed heteropolycyclic group” as used herein refers to a monovalent group having two or more rings condensed to each other, at least one heteroatom other than carbon atoms (for example, having 1 to 60 carbon atoms), as a ring-forming atom, and non-aromaticity in its molecular structure when considered as a whole. Examples of the monovalent non-aromatic condensed heteropolycyclic group include a pyrrolyl group, a thiophenyl group, a furanyl group, an indolyl group, a benzoindolyl group, a naphthoindolyl group, an isoindolyl group, a benzoisoindolyl group, a naphthoisoindolyl group, a benzosilolyl group, a benzothiophenyl group, a benzofuranyl group, a carbazolyl group, a dibenzosilolyl group, a dibenzothiophenyl group, a dibenzofuranyl group, an azacarbazolyl group, an azafluorenyl group, an azadibenzosilolyl group, an azadibenzothiophenyl group, an azadibenzofuranyl group, a pyrazolyl group, an imidazolyl group, a triazolyl group, a tetrazolyl group, an oxazolyl group, an isoxazolyl group, a thiazolyl group, an isothiazolyl group, an oxadiazolyl group, a thiadiazolyl group, a benzopyrazolyl group, a benzimidazolyl group, a benzoxazolyl group, a benzothiazolyl group, a benzoxadiazolyl group, a benzothiadiazolyl group, an imidazopyridinyl group, an imidazopyrimidinyl group, an imidazotriazinyl group, an imidazopyrazinyl group, an imidazopyridazinyl group, an indenocarbazolyl group, an indolocarbazolyl group, a benzofurocarbazolyl group, a benzothienocarbazolyl group, a benzosilolocarbazolyl group, a benzoindolocarbazolyl group, a benzocarbazolyl group, a benzonaphthofuranyl group, a benzonaphthothiophenyl group, a benzonaphthosilolyl group, a benzofurodibenzofuranyl group, a benzofurodibenzothiophenyl group, and a benzothienodibenzothiophenyl group. The term “divalent non-aromatic condensed heteropolycyclic group” as used herein refers to a divalent group having the same structure as a monovalent non-aromatic condensed heteropolycyclic group.

The term “C₆-C₆₀ aryloxy group” as used herein refers to —OA₁₀₂ (wherein A₁₀₂ refers to the C₆-C₆₀ aryl group), and the term “C₆-C₆₀ arylthio group” as used herein refers to —SA₁₀₃ (wherein A₁₀₃ refers to the C₆-C₆₀ aryl group).

R_(10a) may be:

deuterium (-D), —F, —Cl, —Br, —I, a hydroxyl group, a cyano group, or a nitro group; a C₁-C₆₀ alkyl group, a C₂-C₆₀ alkenyl group, a C₂-C₆₀ alkynyl group, or a C₁-C₆₀ alkoxy group, each unsubstituted or substituted with deuterium, —F, —Cl, —Br, —I, a hydroxyl group, a cyano group, a nitro group, a C₃-C₆₀ carbocyclic group, a C₁-C₆₀ heterocyclic group, a C₆-C₆₀ aryloxy group, a C₆-C₆₀ arylthio group, —Si(Q₁₁)(Q₁₂)(Q₁₃), —N(Q₁₁)(Q₁₂), —B(Q₁₁)(Q₁₂), —C(═O)(Q₁₁), —S(═O)₂(Q₁₁), —P(═O)(Q₁₁)(Q₁₂), or any combination thereof;

a C₃-C₆₀ carbocyclic group, a C₁-C₆₀ heterocyclic group, a C₆-C₆₀ aryloxy group, or a C₆-C₆₀ arylthio group, each unsubstituted or substituted with deuterium, —F, —Cl, —Br, —I, a hydroxyl group, a cyano group, a nitro group, a C₁-C₆₀ alkyl group, a C₂-C₆₀ alkenyl group, a C₂-C₆₀ alkynyl group, a C₁-C₆₀ alkoxy group, a C₃-C₆₀ carbocyclic group, a C₁-C₆₀ heterocyclic group, a C₆-C₆₀ aryloxy group, a C₆-C₆₀ arylthio group, —Si(Q₂₁)(Q₂₂)(Q₂₃), —N(Q₂₁)(Q₂₂), —B(Q₂₁)(Q₂₂), —C(═O)(Q₂₁), —S(═O)₂(Q₂₁), —P(═O)(Q₂₁)(Q₂₂), or any combination thereof; or

—Si(Q₃₁)(Q₃₂)(Q₃₃), —N(Q₃₁)(Q₃₂), —B(Q₃₁)(Q₃₂), —C(═O)(Q₃₁), —S(═O)₂(Q₃₁), or —P(═O)(Q₃₁)(Q₃₂).

In the present specification, Q₁ to Q₃, Q₁₁ to Q₁₃, Q₂₁ to Q₂₃, and Q₃₁ to Q₃₃ may each independently be: hydrogen; deuterium; —F; —Cl; —Br; —I; a hydroxyl group; a cyano group; a nitro group; a C₁-C₆₀ alkyl group; a C₂-C₆₀ alkenyl group; a C₂-C₆₀ alkynyl group; a C₁-C₆₀ alkoxy group; or a C₃-C₆₀ carbocyclic group or a C₁-C₆₀ heterocyclic group, each unsubstituted or substituted with deuterium, —F, a cyano group, a C₁-C₆₀ alkyl group, a C₁-C₆₀ alkoxy group, a phenyl group, a biphenyl group, or any combination thereof.

The term “hetero atom” as used herein refers to any atom other than a carbon atom. Examples of the heteroatom include O, S, N, P, Si, B, Ge, Se, or any combination thereof.

The term “Ph” as used herein refers to a phenyl group, the term “Me” as used herein refers to a methyl group, the term “Et” as used herein refers to an ethyl group, the term “ter-Bu” or “Bu^(t)” as used herein refers to a tert-butyl group, and the term “OMe” as used herein refers to a methoxy group.

The term “biphenyl group” as used herein refers to “a phenyl group substituted with a phenyl group.” In other words, the “biphenyl group” is a substituted phenyl group having a C₆-C₆₀ aryl group as a substituent.

The term “terphenyl group” as used herein refers to “a phenyl group substituted with a biphenyl group”. The “terphenyl group” is a substituted phenyl group having, as a substituent, a C₆-C₆₀ aryl group substituted with a C₆-C₆₀ aryl group.

* and *′ as used herein, unless defined otherwise, each refer to a binding site to a neighboring atom in a corresponding formula.

Preparation of Composition Example 1

0.1 g of poly(styrene)-b-poly(methyl methacrylate) (PS-PMMA, molecular weight: 25,000, a value of M₁/M₂ is about 0.25) was dissolved in 10 ml of toluene, and 0.1 g of ZnCl₂ was added to the solution to provide a ZnO quantum dot precursor composition.

Comparative Example 1

A composition was prepared in the same manner as in Example 1, except that, in preparing the composition, polystyrene-poly(2-vinylpyridine (PS—P2VP, molecular weight: 25,000) was used instead of PS-PMMA.

Manufacture of Light-Emitting Device Example 2

ITO 300 Å/Ag 50 Å/ITO 300 Å (anode) was cut to a size of 50 mm×50 mm×0.7 mm, sonicated once with isopropyl alcohol, and once with pure water, for 5 minutes each, and then cleaned by irradiation with ultraviolet rays and exposure of ozone for 30 minutes. The cleaned glass substrate was then introduced into a vacuum deposition apparatus.

A known Compound NPD was vacuum-deposited on the substrate to form a hole injection layer having a thickness of 300 Å, and then TCTA as a hole transporting compound was vacuum-deposited on the NPD layer to form a hole transport layer having a thickness of 200 Å. 9,10-di(naphthalen-2-yl)anthracene (hereinafter, DNA) as a blue fluorescent host and 4,4′-bis[2-(4-(N,N-diphenylamino)phenyl)vinyl]biphenyl (hereinafter, DPAVBi) as a blue fluorescent dopant were applied to the hole transport layer using an inkjet process at a weight ratio of 98:2 to form an emission layer having a thickness of 300 Å.

The composition of Example 1 was coated on the emission layer by inkjet, dried at 100° C., and washed sufficiently using 0.1 M NH₄OH(aq). The coating composition was dried at 100° C. for 10 minutes to form a quantum dot (ZnO)-containing electron transport layer having a thickness of 480 Å. LiF, which is a halogenated alkaline metal, was deposited on the electron transport layer having a thickness of 10 Å, and then, Al was vacuum deposited to form a cathode having a thickness of 3,000 Å to form an LiF/AI electrode, thereby completing the manufacture of a light-emitting device.

Comparative Example 2

A light-emitting device was manufactured in the same manner as in Example 2, except that, in forming an electron transport layer on an emission layer, the composition of Comparative Example 1 was utilized.

Luminescence efficiency of each of the light-emitting devices manufactured according to Example 2 and Comparative Example 2 was measured at 520 nit using a luminance meter PR650, and the results are shown in Table 1.

TABLE 1 Composition Driving Current Half lifespan for hole voltage density Luminance Efficiency Emission (hr @50% transport layer (V) (mA/cm²) (cd/m²) (cd/A) color luminance) Example 2 Example 1 4.4 16.1 520 3.3 Red 2.5 h Comparative Comparative 4.6 40.2 520 1.3 Red   2 h Example 2 Example 1

From Table 1, it may be confirmed that the organic light-emitting device of Example 2 exhibits excellent results compared to the light-emitting device of Comparative Example 2. This is because quantum-dot size distribution is relatively narrow in a quantum dot layer formed using the composition according to an embodiment of the disclosure. In addition, since the quantum-dot precursor distribution is relatively narrow in the composition according to an embodiment of the disclosure, we observed little or no technical issues during the inkjet printing process.

The composition according to an embodiment has an improved dispersion stability, and a light-emitting device of Example 2 including the quantum dot layer formed with the composition of Example 1 has excellent efficiency, i.e., nearly 2.5 times greater efficiency that the device of Comparative Example 2.

It should be understood that embodiments described herein should be considered in a descriptive sense only and not for purposes of limitation. Descriptions of features or aspects within each embodiment should typically be considered as available for other similar features or aspects in other embodiments. While one or more embodiments have been described with reference to the figures, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope as defined by the following claims. 

What is claimed is:
 1. A composition comprising: a block copolymer comprising an A moiety that is hydrophobic solvent-compatible and a B moiety that is hydrophobic solvent-incompatible; a quantum dot precursor; and a hydrophobic solvent, wherein the B moiety that is hydrophobic solvent-incompatible includes a —OH moiety, a —(C═O)O— moiety, or any combination thereof.
 2. The composition of claim 1, wherein the block copolymer is present as a spherical micelle in the composition.
 3. The composition of claim 1, wherein a number average molecular weight of the A moiety is M₂, a number average molecular weight of the B moiety is M₁, and M₁ and M₂ satisfy Equation (1): M₁/M₂≤⅓  (1).
 4. The composition of claim 1, wherein the block copolymer is present as a spherical micelle in the composition, and the B moiety is present in a core of the micelle, and the A moiety is present in a shell of the micelle.
 5. The composition of claim 1, wherein the block copolymer is present as a spherical micelle in the composition, and the quantum dot precursor is present within the spherical micelle.
 6. The composition of claim 1, wherein the block copolymer comprises poly(styrene)-b-poly(methyl methacrylate), poly(styrene)-b-poly(acrylic acid) (PS-PAA), poly(styrene)-b-poly(ethylene glycol), polyethylene glycol-b-polylactic acid (PEG-PLA), poly(ethylene glycol)-b-poly(lactic acid-co-glycolic acid), poly(ethylene glycol)-b-polycaprolactone, polyethylene-block-poly(ethylene glycol), or any combination thereof.
 7. The composition of claim 1, wherein the quantum dot precursor comprises a metallic salt.
 8. The composition of claim 7, wherein the quantum dot precursor comprises a nitrate salt of a metal, a chloride salt of a metal, or any combination thereof.
 9. The composition of claim 1, wherein the quantum dot precursor comprises a metal that is silver, palladium, iron (Fe), cobalt, niobium, molybdenum, tantalum, tungsten, titanium, nickel, copper, cadmium, zinc, indium, tin, a nitrate of one or more of the foregoing metals, a chloride of any one or more of the foregoing metals, or any combination thereof.
 10. The composition of claim 1, wherein the quantum dot precursor comprises AgNO₃, Pd(NO₃)₂, FeCl₃, COCl₂, NbCl₅, MoCl₅, TaCl₅, WCl₅, TiCl₄, NiCl₂, CuCl₂, CdCl₂, ZnCl₂, InCl₃, SnCl₂, or any combination thereof.
 11. The composition of claim 1, wherein the solvent comprises n-hexane, benzene, toluene, dimethylbenzene, ethylbenzene, or any combination thereof.
 12. A method of forming a quantum dot layer, the method comprising: coating a substrate with the composition of claim 1; removing a solvent from the composition of the coated substrate; and treating the composition from which the solvent has been removed with a weak base.
 13. The method of claim 12, wherein the coating of the substrate with the composition is performed by a liquid process.
 14. The method of claim 12, wherein the coating of the substrate with the composition is performed by inkjet printing.
 15. The method of claim 12, wherein the removing of the solvent from the composition coated on the substrate is performed by heating.
 16. The method of claim 12, wherein a pH of the weak base is greater than 7 and less than or equal to
 9. 17. The method of claim 12, wherein the weak base is NH₄OH.
 18. A quantum dot layer formed by the method of forming a quantum dot layer of claim
 12. 19. The quantum dot layer of claim 18, wherein the quantum dot layer is an emission layer or an electron transport layer.
 20. A light-emitting device comprising the quantum dot layer of claim
 18. 